Page 51 - 《摩擦学学报》2021年第3期

340 摩 擦 学 学 报 第 41 卷

Severve delamination
Severve delamination
Small groove

500 μm 500 μm
(a) L=10 N, S=0.75 m/s, 15%Gr/6092Al (b) L=20 N, S=1.00 m/s, (5%Gr+10%SiC p )/6092Al

Fig. 7 Wear morphology of composites with minimum friction coefficient:
图 7 具有最小摩擦系数的复合材料的磨损形貌SEM观察

Small groove
Delamination Small groove
Delamination
Severve delamination
Severve delamination
250 μm 250 μm

(a) L=10 N, S=0.75 m/s, (5%Gr+10%SiC p )/6092Al (b) L=20 N, S=1.00 m/s, (5%Gr+20%SiC p )/6092Al

Fig. 8 SEM micrography of wear morphology of composites with maximum friction coefficient
图 8 具有最大摩擦系数的复合材料的磨损形貌的SEM照片

1.0 1.0 1.0
15%Gr/6092Al 0.8 (10%SiC p +5%Gr)/6092Al 0.8 (20%SiC p +5%Gr)/6092Al
0.8
Friction coefficient 0.6 Friction coefficient 0.6 Friction coefficient 0.6

0.4
0.4
0.4
0.2
0.0
0.0
0.0 0.2 0.2
10 15 20 10 15 20 10 15 20
Load/N Load/N Load/N
(a) 15%Gr/6092Al (b) (10%Gr+5%SiC p )/6092Al (c) (20%SiC p +5%Gr)/6092Al

Fig. 9 Area of friction coefficient of composites under various loads
图 9 不同载荷下复合材料的摩擦系数面积图
图，根据所得面积高度的大小，可以判定摩擦系数的 较于其他两种复合材料，可满足更多的使用条件，具
稳定性，高度越高则稳定性越差. 可以发现3种复合材 有更大的使用潜力. 有文献 也表明硬质陶瓷颗粒体
[31]
料中，15%Gr/6092Al获得了最小摩擦系数，但就摩擦 积分数为15%~20%时，会对复合材料的干滑动行为产

系数稳定性而言，15%Gr/6092Al摩擦系数稳定性最 生积极影响. 当SiC 含量升高时，在磨损过程中，单位
p
差，且随着SiC 体积百分比的增加，摩擦系数稳定性 面积参与磨损的SiC 增多，同时承受了更多载荷，且
p p
提升，也就是说当使用(5%Gr+20%SiC )/6092Al时，相 由于SiC 良好的尺寸稳定性，减少了摩擦系数的波动.
p
p