第 9 期 王梦娇, 等: 激光微织构排布方式对铝青铜摩擦学性能影响研究 1325

(a1) Substrate (b1) Oval-L (c1) Oval-S (d1) Triangle-L

Sliding direction Sliding direction
Sliding direction Sliding direction
300 μm 300 μm 300 μm 300 μm

(a2) (b2) (c2) (d2)
Groove
Pit
Pit
30 μm 30 μm 30 μm 30 μm

(e1) Triangle-S (f1) T+O-L (g1) T+O-S

Sliding direction
Sliding direction

300 μm 300 μm 300 μm

(e2) (f2) (g2)
Pit

30 μm 30 μm 30 μm

Fig. 8 SEM micrographs of worn morphology of substrate and textured CuAl10Fe5Ni5 samples under dry friction: (a) substrate;
(b) oval-L; (c) oval-S; (d) triangle-L; (e) triangle-S; (f) T+O-L; (g) T+O-S
图 8 干摩擦下基材和织构化CuAl10Fe5Ni5试样表面磨损形貌的SEM照片：(a) 基材；(b) 椭圆-线性；(c) 椭圆-交错；
(d) 三角形-线性；(e) 三角形-交错；(f) 椭圆+三角形-线性；(g) 椭圆+三角形-交错

1 165 μm 1 086 μm 1 074 μm 1 079 μm

300 μm 300 μm 300 μm 300 μm
(a) Substrate (b) Oval-L (c) Oval-S (d) Triangle-L

1 076 μm 1 152 μm 1 092 μm

300 μm 300 μm 300 μm
(e) Triangle-S (f) T+O-L (g) T+O-S
Fig. 9 Optical micrographs of worn morphology of GCr15 steel ball under dry friction: (a) substrate; (b) oval-L; (c) oval-S;
(d) triangle-L; (e) triangle-S; (f) T+O-L; (g) T+O-S
图 9 干摩擦情况GCr15钢球在光学显微镜下磨损形貌照片：(a) 基材；(b) 椭圆-线性；(c) 椭圆-交错；
(d) 三角形-线性；(e) 三角形-交错；(f) 椭圆+三角形-线性；(g) 椭圆+三角形-交错