Page 87 - 《摩擦学学报》2021年第5期

676 摩 擦 学 学 报 第 41 卷

表 3 吸附性能测试中钢芯片频率变化值
Table 3 The values of copper chip frequency change during adsorption measurements

△f soaked in different ionic liquid solution/Hz
Lubricant’s concentrations
[Ch] 2 [2,5-Fdc] [Ch] 2 [2,5-Tdc] [Ch] 2 [2,3-Pydc] [Ch] 2 [2,6-Pydc] [Ch] 2 [3,4-Pydc] [Ch] 2 [3,5-Pydc] [Ch] 2 [2,3-Pyadc]
0.2 mol/L 41.530 47.980 43.560 42.630 42.620 42.790 41.470
1.667 mol/L 1 343.860 1 048.360 1 255.070 1 080.820 1 204.460 1 000.610 1 131.900

A1 B1[Ch] 2 [2,5-Fdc] C1[Ch] 2 [2,5-Tdc] D1[Ch] 2 [2,3-Pydc] E1[Ch] 2 [2,6-Pydc] F1[Ch] 2 [3,4-Pydc] G1[Ch] 2 [3,5-Pydc] H1[Ch] 2 [2,3-Pyadc]

Unsoaked
cast iron Soaked cast iron bars in 0.2 mol/L ionic liquid solution
bars

A2 B2[Ch] 2 [2,5-Fdc] C2[Ch] 2 [2,5-Tdc] D2[Ch] 2 [2,3-Pydc] E2[Ch] 2 [2,6-Pydc] F2[Ch] 2 [3,4-Pydc] G2[Ch] 2 [3,5-Pydc] H2[Ch] 2 [2,3-Pyadc]

Soaked cast iron
Soaked cast iron bars in 1.667 mol/L ionic liquid solution
bars in pure water

Fig. 6 The graph of cast iron bars soaked in pure water and aqueous solutions with varying concentrations of [Ch] 2 [Hdc]
图 6 浸泡在纯水和含不同浓度[Ch] 2 [Hdc]的水溶液中的铸铁条的照片

铁条的腐蚀程度分为A-D四个等级，A：不生锈，光泽 给出了铸铁条在腐蚀前后的表面粗糙度变化情况. 由
好如新；B：没有生锈，只是光损耗；C：轻微腐蚀、失 表中数据可以看出，浸泡在纯水溶液中的铸铁条表面
光；D：腐蚀或严重失光. 从上图可以看出，浸没在 粗糙度在腐蚀前后发生了较大程度的改变，其表面粗

0.2和1.667 mol/L[Ch] [Hdc]水溶液中的铸铁棒均未发 糙度值由腐蚀前的0.436 μm升高到了1.634 μm，表明
2
现明显腐蚀，而浸泡在纯水溶液中的铸铁条表面腐蚀 铸铁条表面有较为严重的腐蚀. 而浸泡在含0.2和
严重，表明该类离子液体可显著降低水的腐蚀性. 表4 1.667 mol/L的[Ch] [Hdc]水溶液中的铸铁棒的表面粗
2