Page 26 - 《爆炸与冲击》2026年第10期

第 46 卷 叶想平，等： 辐照-预应力和冲击耦合作用下金属硬化和脆化规律与微观机理实验研究进展 第 10 期

1.25 With tensile stress 25%σ 0.2 2.8 Without tensile stress

Void number density/(10 20 m −3 ) 0.75 Without tensile stress Dislocation loop density/(10 20 m −3 ) 1.4 With tensile stress 10%σ 0.2
1.00
2.1

0.50
0.7
0.25

0 15 30 45 60 75 0 40 80 120 160
Void diameter/nm Dislocation loop diameter/nm
(a) Voids distribution (b) Dislocation loops distribution
图 11 预拉伸应力中子辐照退火态 316 不锈钢中缺陷分布 [12]
Fig. 11 Distribution of defects in irradiation pre-tension stressed 316 annealed stainless steel [12]
1.0

0.8
Normalized loopdensity 0.6

0.4

0.2

0
0 50 100 150 200
Resolved normal stress/MPa
图 12 沿位错环外法向分解主应力对位错环数密度的影响 [20]
Fig. 12 Effect of principal stress decomposition along the outer normal direction of dislocation loops
on dislocation loop number density [20]

(100) [010]

(111) R 1 Particles

(100)
τ
R 2 (111)
(010) [100]
(010)
Dislocations [001]
R 3
图 13 滑移位错绕行通过不同取向性分布位错环时最小弓弯半径示意图 [21]
Fig. 13 Schematic of dislocation bypassing hard obstacles with different distributions at critical time [21]

3 辐照金属的动态硬化和脆化行为

由于材料动态力学性能实验研究自身实验技术复杂性（实验装置调试、样品安装均需要人员近距离
精细化操作等）与中子辐照金属 γ 射线防护（中子辐照过程中，部分金属原子核俘获中子生成不稳定的

101101-10